VM SPARKLE Description Film: 100 micron (including adhesive) Pearl White (Matte), Monomeric Calendered PVC film Adhesive: Permanent Clear Solvent based Acrylic adhesive Release liner: One Side PE and Silicon Coated Kraft Paper, 14Ogsm Width: 1.02/1.06/1.27/1.52m Length: 50 mtrs Shelf Life: Up to 2 year at 20 C and relative humidity of 50% Durability: Upto 1 year TECHNICAL DATA SHEET Data Sheet Item Unit Value Tested Method Thickness- Film μm 100 GB/T6672-2001 Thickness- Finished Product μm 235 GB/T6672-2001 Adhesive Weight g/m 17-22 FINAT12 Elongation at Break MD % >100 GB/T1040.1-2006 Elongation at Break CD % >70 GB/T1040.1-2006 Tensile Strength at Break MD N/25mm 40-50 GB/T1040.1-2006 Tensile Strength at Break CD N/25mm 35-45 GB/T1040.1-2006 Dimesnsional Stability MD % <1.5 FINAT14 Dimesnsional Stability CD % <1.0 FINAT14 Initial Adhesion N/25mm >7 FINAT9 180 Peel -20 Minutes N/25mm >7 FINAT9 180 Peel -24 Hours N/25mm >9 FINAT1 Applied Printers : Inkjet printing with Solvent/ ECO Solvent based inks, UV or Latex inks Declaration:Please choose VAGUS products suitably according to relative provisions or industrial standards. VAGUS bears the responsibility for the specified technical and performance data on this page only. VAGUS is not responsible for any other liability. (The technical data on this page is calculated on average, and ±5% tolerance is acceptable)
VM SPARKLE Description Film: 100 micron (including adhesive) Pearl White (Matte), Monomeric Calendered PVC film Adhesive: Permanent Clear Solvent based Acrylic adhesive Release liner: One Side PE and Silicon Coated Kraft Paper, 14Ogsm Width: 1.02/1.06/1.27/1.52m Length: 50 mtrs Shelf Life: Up to 2 year at 20 C and relative humidity of 50% Durability: Upto 1 year TECHNICAL DATA SHEET Data Sheet Item Unit Value Tested Method Thickness- Film μm 100 GB/T6672-2001 Thickness- Finished Product μm 235 GB/T6672-2001 Adhesive Weight g/m 17-22 FINAT12 Elongation at Break MD % >100 GB/T1040.1-2006 Elongation at Break CD % >70 GB/T1040.1-2006 Tensile Strength at Break MD N/25mm 40-50 GB/T1040.1-2006 Tensile Strength at Break CD N/25mm 35-45 GB/T1040.1-2006 Dimesnsional Stability MD % <1.5 FINAT14 Dimesnsional Stability CD % <1.0 FINAT14 Initial Adhesion N/25mm >7 FINAT9 180 Peel -20 Minutes N/25mm >7 FINAT9 180 Peel -24 Hours N/25mm >9 FINAT1 Applied Printers : Inkjet printing with Solvent/ ECO Solvent based inks, UV or Latex inks Declaration:Please choose VAGUS products suitably according to relative provisions or industrial standards. VAGUS bears the responsibility for the specified technical and performance data on this page only. VAGUS is not responsible for any other liability. (The technical data on this page is calculated on average, and ±5% tolerance is acceptable)
Description Film: 100 micron (including adhesive) Pearl White (Matte), Monomeric Calendered PVC film Adhesive: Permanent Clear Solvent based Acrylic adhesive Release liner: One Side PE and Silicon Coated Kraft Paper, 14Ogsm Width: 1.02/1.06/1.27/1.52m Length: 50 mtrs Shelf Life: Up to 2 year at 20 C and relative humidity of 50% Durability: Upto 1 year TECHNICAL DATA SHEET Data Sheet Item Unit Value Tested Method Thickness- Film μm 100 GB/T6672-2001 Thickness- Finished Product μm 235 GB/T6672-2001 Adhesive Weight g/m 17-22 FINAT12 Elongation at Break MD % >100 GB/T1040.1-2006 Elongation at Break CD % >70 GB/T1040.1-2006 Tensile Strength at Break MD N/25mm 40-50 GB/T1040.1-2006 Tensile Strength at Break CD N/25mm 35-45 GB/T1040.1-2006 Dimesnsional Stability MD % <1.5 FINAT14 Dimesnsional Stability CD % <1.0 FINAT14 Initial Adhesion N/25mm >7 FINAT9 180 Peel -20 Minutes N/25mm >7 FINAT9 180 Peel -24 Hours N/25mm >9 FINAT1 Applied Printers : Inkjet printing with Solvent/ ECO Solvent based inks, UV or Latex inks Declaration:Please choose VAGUS products suitably according to relative provisions or industrial standards. VAGUS bears the responsibility for the specified technical and performance data on this page only. VAGUS is not responsible for any other liability. (The technical data on this page is calculated on average, and ±5% tolerance is acceptable)
