VG POLYMERIC GXR Description Film: 95 micron (including adhesive) White (Gloss), Polymeric PVC film Adhesive: Removable Grey Solvent based Acrylic adhesive Release liner: Air Free, One Side PE and Silicon Coated Kraft Paper, 140gsm Width: 1.02/1.06/1.27/1.52m Length: 50 mtrs Durability: Upto 3 year TECHNICAL DATA SHEET Data Sheet Item Unit Value Tested Method Thickness- Film μm 70 GB/T6672-2001 Thickness- Finished Product μm 235 GB/T6672-2001 Adhesive Weight g/m 26-28 FINAT12 Elongation at Break MD % >180 GB/T1040.1-2006 Elongation at Break CD % >140 GB/T1040.1-2006 Tensile Strength at Break MD N/25mm 55-70 GB/T1040.1-2006 Tensile Strength at Break CD N/25mm 45-60 GB/T1040.1-2006 Dimesnsional Stability MD % <0.4 FINAT14 Dimesnsional Stability CD % <0.3 FINAT14 Initial Adhesion N/25mm FINAT9 180 Peel -20 Minutes N/25mm 5-7 FINAT9 180 Peel -24 Hours N/25mm 9-12 FINAT1 Applied Printers : Inkjet printing with Solvent/ ECO Solvent based inks, UV or Latex inks Declaration:Please choose VAGUS products suitably according to relative provisions or industrial standards. VAGUS bears the responsibility for the specified technical and performance data on this page only. VAGUS is not responsible for any other liability. (The technical data on this page is calculated on average, and ±5% tolerance is acceptable)
VG POLYMERIC GXR Description Film: 95 micron (including adhesive) White (Gloss), Polymeric PVC film Adhesive: Removable Grey Solvent based Acrylic adhesive Release liner: Air Free, One Side PE and Silicon Coated Kraft Paper, 140gsm Width: 1.02/1.06/1.27/1.52m Length: 50 mtrs Durability: Upto 3 year TECHNICAL DATA SHEET Data Sheet Item Unit Value Tested Method Thickness- Film μm 70 GB/T6672-2001 Thickness- Finished Product μm 235 GB/T6672-2001 Adhesive Weight g/m 26-28 FINAT12 Elongation at Break MD % >180 GB/T1040.1-2006 Elongation at Break CD % >140 GB/T1040.1-2006 Tensile Strength at Break MD N/25mm 55-70 GB/T1040.1-2006 Tensile Strength at Break CD N/25mm 45-60 GB/T1040.1-2006 Dimesnsional Stability MD % <0.4 FINAT14 Dimesnsional Stability CD % <0.3 FINAT14 Initial Adhesion N/25mm FINAT9 180 Peel -20 Minutes N/25mm 5-7 FINAT9 180 Peel -24 Hours N/25mm 9-12 FINAT1 Applied Printers : Inkjet printing with Solvent/ ECO Solvent based inks, UV or Latex inks Declaration:Please choose VAGUS products suitably according to relative provisions or industrial standards. VAGUS bears the responsibility for the specified technical and performance data on this page only. VAGUS is not responsible for any other liability. (The technical data on this page is calculated on average, and ±5% tolerance is acceptable)
Description Film: 95 micron (including adhesive) White (Gloss), Polymeric PVC film Adhesive: Removable Grey Solvent based Acrylic adhesive Release liner: Air Free, One Side PE and Silicon Coated Kraft Paper, 140gsm Width: 1.02/1.06/1.27/1.52m Length: 50 mtrs Durability: Upto 3 year TECHNICAL DATA SHEET Data Sheet Item Unit Value Tested Method Thickness- Film μm 70 GB/T6672-2001 Thickness- Finished Product μm 235 GB/T6672-2001 Adhesive Weight g/m 26-28 FINAT12 Elongation at Break MD % >180 GB/T1040.1-2006 Elongation at Break CD % >140 GB/T1040.1-2006 Tensile Strength at Break MD N/25mm 55-70 GB/T1040.1-2006 Tensile Strength at Break CD N/25mm 45-60 GB/T1040.1-2006 Dimesnsional Stability MD % <0.4 FINAT14 Dimesnsional Stability CD % <0.3 FINAT14 Initial Adhesion N/25mm FINAT9 180 Peel -20 Minutes N/25mm 5-7 FINAT9 180 Peel -24 Hours N/25mm 9-12 FINAT1 Applied Printers : Inkjet printing with Solvent/ ECO Solvent based inks, UV or Latex inks Declaration:Please choose VAGUS products suitably according to relative provisions or industrial standards. VAGUS bears the responsibility for the specified technical and performance data on this page only. VAGUS is not responsible for any other liability. (The technical data on this page is calculated on average, and ±5% tolerance is acceptable)
